司太立耐熱磨硬質(zhì)合金的物理力學性能
| 名稱 | 物理性能 | 力學性能 | ||||||
| 相對 密度 |
熔點/℃ | 比熱熔J·(kg·℃) | 熱膨脹系數(shù)（50～600℃）/μm·(m·℃) -1 | 彈性模量 MPa |
抗拉強度 MPa |
抗壓強度 MPa |
硬度① （常溫） |
|
| No1 | 8.48 | 1265 | 393.5592 | 13.8 | 253500 | 780 | 1610 | 54HRC (G) |
| No6 | 8042 | 1290 | 422.8668 | 14.9 | 210000 | 940 | 1730 | 44 HRC (G) |
| No12 | 8047 | 1285 | 410.3064 | 14.4 | 204000 | 990 | 1810 | 47 HRC (G) |
| No21 | 8030 | 1350 | 422.8668 | 14.9 | 820 | 33 HRC (D) [45 HRC] |
||
| No25 | 9.13 | 1410 | 385.1856 | 14.8 | 240000 | 1030 | 20 HRC [41 HRC] |
|
| No32 | 8.68 | 1300 | 14.1 | 790 | 2040 | 42 HRC (G) | ||
| No711 | 8.06 | 1265 | 13.6 | 540 | 1590 | 40 HRC (G) | ||
| No1016 | 9.00 | 1265 | 12.0 | 630 | 1680 | 57 HRC (G) | ||
| O合金 | 8.79 | 1270 | 389.3724 | 13.0 | 440 | 61 HRC (G) | ||
| No40 | 7.80 | 1038 | 210 | 57 HRC (G) | ||||
| No41 | 8.14 | 1066 | 380 | 51 HRC (G) | ||||
| 哈氏合金C | 8.94 | 1290 | 385.1856 | 13.7 | 180000 | 750 | 96 HRC (D) [35 HRC] |
|
| No90 | 7.35 | 1310 | 460.548 | 14.9 | 630 | 47 HRC 56 HRC (G) |
||
| No93 | 7.77 | 1178 | 460.548 | 12.8 | 630 | 57 HRC (D) 62 HRC (G) |
||
注：力學性能是試驗的結(jié)果。
① G-氣焊； D-由暴富電弧焊接造成的余量厚度； []內(nèi)的硬度表示加工硬化后的硬度。